ISO X6CrNiNb18-10
2014-03-03 17:24:40 Print this pageThe high quality International ISO X6CrNiNb18-10 material is one of the more steel grades we supply, ISO ISO 15510 (2010), ISO ISO 16143-1 (2004), ISO ISO 16143-2 (2004), ISO ISO 9327-5, ISO ISO 9328-5, ISO ISO 9328-7 (2011), ISO ISO 9329-4, ISO ISO 9330-6, ISO ISO/TS 15510 (2003),Stainless steels - Chemical composition. X6CrNiNb18-10 is our main production grade, which has been approved by customers in many countries since its initial production, including our X6CrNiNb18-10 round bars, flat bar, forgings, fasteners, tubes, wires, strips, sheets & Plates, as well as a variety of profiles, professional high precision auto-lathe processing manufacturer of clinching fasteners, axes, standoffs, screws, studs, nuts, bolt, OEM parts and special shaped turning partsthe state of delivery includes quenched and tempered, annealed, machined semi-finished products, we also have strict management of the packaging, to avoid material damage from transportation. We are the best supplier of X6CrNiNb18-10 materials, and we are willing to develop together with customers from all over the world.
Also includes X6CrNiNb18-10 steel material norm, chemical composition, mechanical properties, datasheet, X6CrNiNb18-10 equivalent, heat treatment and temperature process of X6CrNiNb18-10, The peak hardness can be achieved, Contains all of the specification, welding properties, let us in X6CrNiNb18-10 this steel grade have a more comprehensive understanding, Download the full X6CrNiNb18-10 PDF version of this datasheet.
Chemical composition (wt.%) of X6CrNiNb18-10
Elements | Min.(≥) | Max.(≤) |
---|---|---|
C | - | 0.08 |
Si | - | 1.00 |
Mn | - | 2.00 |
P | - | 0.045 |
S | - | 0.030 |
Cr | 17.00 | 19.00 |
Ni | 9.00 | 12.00 |
Mo | - | - |
N | - | - |
Nb | 10×C% | 1.00 |
Mechanical Properties of X6CrNiNb18-10
Rp0.2 (MPa) | Rm (MPa) | Impact KV (J) |
Elongation A (%) |
A Z (%) | Delivery | Hardness HB |
---|---|---|---|---|---|---|
928 (≥) | 937 (≥) | 43 | 33 | 11 | Solution & Aging, Ann, Ausaging, Q+T | 121 |